氧化铝陶瓷胶 耐磨管道贴片胶 环氧树脂ab胶

产品介绍： 

 本品为双组份增韧高度度型膏状环氧粘结剂,具有高度度结构性粘结、优异的耐冲击性能、触变性好、耐高温、耐磨损、耐腐蚀、低温固化等特点，尤其在高温等恶劣工况下仍保持较高的粘结强度。广泛应用于各种陶瓷片与金属的粘接,也可用于立面施工。初粘力强,施工过程中不用磁铁或其他支撑措施而不脱落,优化了施工工艺,降低施工成本。

1．A:B=1:1，施工简便快捷，低气味。

2．A、B两组份混后成膏状，粘度高，不流淌，耐老化，耐水性好，触变性好，冬季易调胶。

3．室温固化快，粘接强度高。

         1. General type,proportion1:1 ,easy mixed,low odor.

         2. Fast curing with room temperature,High bonding strength,Good toughness,

High impact strength.

3. A, B were mixed into a paste,high viscosity,not flow on vertical surface.

应用领域:广泛应用于各种耐磨陶瓷片与金属的粘接，如火电厂的输煤、制粉、排灰、除尘系统及冶炼钢铁厂的输料、配料系统，料斗、料仓、耐磨管道、弯头、球磨机等。

Applications：It is widely used for bonding various wear-resisting ceramic sheets to metals, such as coal conveying, powder making, ash removal, dust removal system in thermal power plants, feeding and proportioning system in smelting iron and steel plants, hopper, silo, wear-resisting pipeline, elbow, ball mill, etc.

性能特点：★.粘接强度高、韧性好；★.由改性耐热增韧树脂及特种固化剂组成；★.耐高温、耐介质、耐腐蚀、韧性好、耐老化(可达8年以上)；★.可常温固化，也可加热固化。

    我公司陶瓷片胶：配胶便利、施工便捷、用量减少，为客户降低了人工和材料成本。
   1:1配比和更薄的施胶厚度令客户一目了然，方便了客户配胶施胶，节省了胶的用量。固化后粘接更牢固，耐温更高。提升了胶品质的同时也为客户降低了成本，提升了工程质量为客户免去不必要的麻烦。

使用说明：

         广泛应用于各种陶瓷片与金属的粘接，也可用于立面施工。初粘力强，施工过程中不用磁铁或其他支撑措施而不脱落，优化了施工工艺，降低了施工成本。

使用方法：

1.表面处理：打磨或喷砂去除被粘物表面的灰尘、油污及锈迹。(如果对强度要求较高,用丙酮等清洗剂清洗干净并燥)。 

2.配胶：A、B组份按配比1:1配胶,搅拌均匀使颜色一致(每次配胶不宜过多,配胶后应尽快用完。胶液凝胶时间也与温度有关,温度越高，凝胶越快)。

 3.施胶：调匀后均匀(忌太多)涂于已处理好的待粘表面，把陶瓷片需要粘接的那一面清洁（可用湿布把表面的氧化铝粉等抹掉,晾干后施用）,然后将两接触面合拢并施加接触压力,胶层厚度为1毫米左右为宜。 

 4.固化：室温50min初固，8～10小时可基本达到结构强度，24h完全固化。[若再加热至60℃—80℃保温2h进行后固化,可得更高的综合性能（可提高30%）]。

 5.注意事项：

   ①此胶混合后,在25℃条件下,有半小时左右的适用期。

    ②每次配胶不宜过多，配胶后应尽快用完【可有半小时的适用期(适用期是指胶未变稠,适合进行粘贴操作的期间)】。

   ③如在储存期内某组份分层属于正常现象,请在使用前进行搅拌预混。

④避免接触外表，眼睛，不慎粘附在外表上,可用酒精或肥皂清洗,再用清水清洗洗干净。如不慎误入眼中,应立即用清水清洗后就医。

1.Remove oil, dirt, rust and polishing rough for the bonding surfaces, Using acetone, ethyl acetate and other cleaning agent to make it clean and dry.

2.Mixing  part A and part B thoroughly according to the regulated ratio till the uniform color achieve, mixed thoroughly and coated on the processed surfaces to be sticky, then put the two contact surfaces together and the contact pressure applied, 8 ~ 10 hours to reach the structure strength, the bonded objects can be used and moved.

3.Room temperature 25℃ ,after mixed the glue should be used within 30minutes

4.Each time mixed suitable quantity glue, adhesive should be used up as quickly as possible. Glue gel time is related to the temperature, the higher the temperature, the faster the glue gel.

5.Avoid contact with skin, eyes,accidentallyadhered to the skin, use alcohol or washing soap rinse clean. Accidentally strayed into the eyes, rinse immediately with plenty of water ,then see the doctor

淄博新润清化工有限公司是一家有经验生产氧化铝耐磨陶瓷和耐磨陶瓷片胶为主的综合性私营企业,公司坐落于四大瓷都之一淄博市。我公司占地面积2000多平方米,厂房总建筑面积1000多平米,现有员工20余人,是国内氧化铝陶瓷主要生产厂家之一。常年致力于耐磨陶瓷材料的技术开发、产品设计制造以及现场施工。具备严格质量控制体系,从原料选购,配料,生产工艺管理到出厂检验控制等各个环节保证产品性能稳定,质量过硬。可以及时为您提供各种解决磨损问题的系统方案,依据实际工况,选择恰当的耐磨材料与施工方案。合理化产品设计、稳定高质量工厂制造及现场施工、售后服务的完善，助您有效提高设备运营效率和使用寿命。我们秉承“真诚面对客户和员工，发展依靠团队”之理念，坚持“客户至上”的原则为广大客户提供优异的服务。欢迎惠顾。