斯米克S201铜焊丝
Category
类 别
Trademark
牌 号
Chemical composition
主要成份(%)
Characteristics & application
特性和用途
Equivalent to AWS
相当AWS
Hardfacing
硬
面
堆
焊
S 101
C3 Cr28 Ni4Si3.5 Fe Rem.
HRc48-54. Resistance to wear, gas corrosion and oxidation. Hardfacing of bucket tooth and case pump.HRc48-54，耐磨、耐气蚀、抗氧化。堆焊铲斗齿，泵套
S 111
C1 Cr29 W5Co Rem.
HRc38-47. Resistance to wear and corrosion at high-temperature. Hardfacing of high temperature and pressure valve.HRc38-47，高温下耐磨、耐蚀。堆焊高温高压阀门
ECoCr-A
S 112
C1.5 Cr29 W8Co Rem.
HRc45-50. Resistance to wear and corrosion at high-temperature. Hardfacing of valve and hot-rolling pass.HRc45-50，高温下耐磨、耐蚀。堆焊阀门，热轧孔型
ECoCr-B
S 113
C2.5 Cr30 W17Co Rem.
HRc≥55. Wear and heat resistance at high temperature, bad shock resistance. Hardfacing of screw charging carriage.HRc≥55，高温下耐磨、耐热，但抗冲击性差。堆焊螺旋送料机用
S 114
C2.5 Cr30 W12Co Rem.
HRc≥53. Wear and heat resistance at high temperature, bad shock resistance. Hardfacing of three-cone bit.HRc≥53，高温下耐磨、耐热，但抗冲击较差。堆焊牙轮钻头
ECoCr-C
Copper
alloys
铜
合
金
S 201
Sn1 Si0.3Mn0.3Cu Rem.
Good mechanical properties and crack resistance. Gas welding and argon arc welding of red copper.机械性能好，抗裂性好。紫铜气焊及氩弧焊用
ERCu
S 211
Si3 Mn1Cu Rem.
Good mechanical properties. Argon arc welding of copper alloys and MIG brazing of steel.机械性能好，铜合金氩弧焊及钢的MIG钎焊用
ERCuSi-Al
S 212
Sn5 Cu Rem.
Wear resistance. Argon arc welding of copper alloys and surfacing of steel.耐磨性好。铜合金氩弧焊及钢的堆焊用
ERCuSn-A
S 213
Sn8 Cu Rem.
Wear resistance. Argon arc welding of copper alloys and surfacing of steel.耐磨性好。铜合金氩弧焊及钢的堆焊用
ERCuSn-C
S 214
Al7.5 Cu Rem.
Wear and corrosion resistance. Argon arc welding of copper alloys and surfacing of steel.耐磨、耐蚀。铜合金氩弧焊及钢的堆焊用
ERCuAl-A1
S 215
Al9 Cu Rem.
Wear and corrosion resistance. Argon arc welding of copper alloys and surfacing of steel.耐磨、耐蚀。铜合金氩弧焊及钢的堆焊用
ERCuAl-A2
S 221
Cu60 Sn1 Si0.3Zn Rem.
Melting point is about 890℃. Gas welding and carbon arc welding of brass, also braze welding of copper, steel and cast iron.熔点约890℃。黄铜气焊及碳弧焊用，也可钎焊铜、钢、铸铁
S 221F
Cu60 Sn1 Si 0.3Zn Rem.
S221 welding rod coated with flux.外涂焊剂的S221焊丝
S 222
Cu58Sn0.9Si0.1Fe0.8 Zn Rem.
Melting point is about 880℃. Gas welding and carbon arc welding of brass, also braze welding of copper, steel and cast iron.熔点约880℃。黄铜气焊及碳弧焊用，也可钎焊铜、钢、铸铁
RBCuZn-C
S 222F
Cu58Sn0.9Si0.1Fe0.8 Zn Rem.
S222 welding rod coated with flux.外涂焊剂的S222焊丝
RBCuZn-C
S 223
Cu59 Sn0.6Zn Rem.
Melting point is about 900℃. Braze welding of copper, steel and cast iron.熔点约900℃。铜、钢、铸铁钎焊用
RBCuZn-A
S 224
Cu62 Si0.5Zn Rem.
Melting point is about 905℃. Gas welding and carbon arc welding of brass, also braze welding of copper, steel and cast iron.熔点约905℃。黄铜气焊及碳弧焊用，也可钎焊铜、钢、铸铁
Copperalloys
铜
合
金
S 225
Cu48 Ni10Zn Rem.
Melting point is about 935℃ and high strength. Braze welding of steel, nickel and carbide alloys.熔点约935℃。高强度,钎焊钢、镍及硬质合金用
RBCuZn-D
S 225F
Cu48 Ni10Zn Rem.
S225 welding rod coated with flux.外涂焊剂的S225焊丝
RBCuZn-D
S 226
Cu60 Sn0.3Si0.2 Zn Rem.
Melting point is about 900℃. Gas welding of brass, also braze welding of copper, steel and cast iron.熔点约900℃。黄铜气焊用，也可钎焊铜、钢、铸铁
S 227
Cu58Sn0.9Ni0.5Si0.1 Fe0.8Zn Rem.
Melting point is about 880℃. Gas welding and carbon arc welding of brass, also braze welding of copper, steel and cast iron.熔点880℃。黄铜气焊及碳弧焊用，也可钎焊铜、钢、铸铁
RBCuZn-B
S 229
Cu55 Ni6 Mn4Zn余
Melting point is about 920℃, high strength. Braze welding of steel, nickel and hard carbide.熔点约920℃。高强度,钎焊钢、镍及硬质合金用
Aluminum alloys
铝
合
金
S 301
Al≥99.5
Good ductility and corrosion resistance. Gas welding and argon arc welding of pure aluminum.塑性好、耐蚀。纯铝气焊、氩弧焊用
ER1100
S 311
Si5 Al Rem.
Corrosion resistance, wide range of usage. Gas welding and argon arc welding of aluminum alloys other than high magnesium alloys.抗裂性好，通用性大。铝合金气焊、氩弧焊用。不宜用高镁合金
ER4043
S 321
Mn1.3 Al Rem.
Good corrosion resistance, weldability and ductility. Gas welding and argon arc welding of aluminum alloys.良好的耐蚀性、可焊性及塑性。铝合金气焊、氩弧焊用
S 331
Mg5 Mn0.4Al Rem.
Corrosion resistance and high strength. Argon arc welding of aluminum alloys.耐蚀，强度高。铝合金氩弧焊用
ER5183